Caverna™ PP

Caverna™ PP

$110

1.75mm diameter

500g spool

 

$110

 

Spool Dimensions: 20 x 5.5 cm

Package Weight: 1.1 kg

Filament Diameter: 1.75 mm

Spool Weight: 500 g

Extruder temperature: 220-250˚ C

Build plate temperature:  RT-50˚ C

Chamber temperature: Not required

2.85mm diameter

500g spool

 

$110

 

Spool Dimensions: 20 x 5.5 cm

Package Weight: 1.1 kg

Filament Diameter: 2.85 mm

Spool Weight: 500 g

Extruder temperature: 220-250˚ C

Build plate temperature:  RT-50˚ C

Chamber temperature: Not required

1 kg pellets

 

$60

 

Weight: 1 kg

Extruder temperature: 220-250˚ C

Build plate temperature:  RT-50˚ C

Chamber temperature: Not required

5 kg pellets

 

$250

 

Weight: 5 kg

Extruder temperature: 220-250˚ C

Build plate temperature:  RT-50˚ C

Chamber temperature: Not required

10 kg pellets

 

$425

 

Weight: 10 kg

Extruder temperature: 220-250˚ C

Build plate temperature:  RT-50˚ C

Chamber temperature: Not required

 

 

Glass (use an AquaSys 120 raft or PP build plate adhesive for best results), PEI

PP, Aquasys 120

Store in sealed bag in a cool, dry location when not in use. 

Print Head: 220-250ºC
Build Plate: RT-50ºC
Chamber: RT-50ºC

50-804-496-8249ºC in agitated water until soluble phase is completely dissolved.

The statements, technical information and recommendations contained herein are believed to be accurate as of the date hereof. Since the conditions and methods of use of the product and of the information referred to herein are beyond our control, Infinite Material Solutions, LLC. Expressly disclaims any and all liability as to any results obtained or arising from any use of the product or reliance on such information: NO WARRANTY OF FITNESS FOR ANY PARTICULAR PURPOSE, WARRANTY OF MERCHANTABILITY OR ANY OTHER WARRANTY, EXPRESSED OR IMPLIED, IS MADE CONCERNING THE GOODS DESCRIBED OR THE INFORMATION PROVIDED HEREIN. The information provided herein relates only to the specific product described and may not be applicable when such product is used in combination with other materials or in any process. The user should thoroughly test any application before commercialization. Nothing contained herein constitutes a license to practice under any patent and it should not be construed as an inducement to infringe any patent and the user.